1 Hoolauna
ʻO ka carbon fiber reinforced epoxy composite (CFRP) he nui nā pono e like me ka haʻahaʻa haʻahaʻa, ka ikaika kikoʻī kiʻekiʻe, ka paʻakikī kikoʻī kiʻekiʻe, ke kūpaʻa luhi, ka pale ʻana i ka corrosion a me nā waiwai mechanical maikaʻi. Hoʻohana nui ʻia ia i ka aerospace a me nā hale hana ʻino ʻē aʻe, ka wela wela a me ka hopena. Ke ʻike nui ʻia nei ka hopena o nā mea kaiapuni i nā mea. I nā makahiki i hala iho nei, ua hoʻokō ka poʻe ʻepekema kūloko a me nā haole i ka nui o nā haʻawina e pili ana i nā hopena o ka wela a me ka haʻahaʻa ma luna o CFRP composites [1] a me ka hopena o ka hopena i nā CFRP composites. Ua ʻike ka haʻawina ʻo ka mana o ka wela a me ka humid kaiapuni ma CFRP composites e pili ana i ka plasticization o ka matrix [2, ka haʻihaʻi [31 a me ka nāwaliwali o ka fiber-matrix interface waiwai [2'3'5], CFRP composite kulou me ka hoʻonui ʻana i ka manawa wela wela) ʻO nā mea mechanical o ka hana [2, ke alakaʻi a me ka interlaminar shear waiwai [2, 1 a me ka static tensile'7 i hōʻike ʻia [3 a' static tensile'7]. Woldesenbet et al. Ua aʻo ʻo [8,9] i ka hopena mechanical properties o nā composites ma ke kiʻekiʻe o ke kaumaha ma hope o ka hoʻomaʻamaʻa ʻana i ka wela, a loaʻa iā ia ua hoʻomaikaʻi ke kaiapuni wela a me ka haʻahaʻa i ka ikaika o ka hopena o nā composites. Ua hōʻike ʻia e hiki ke hoʻomaikaʻi i ka hoʻomaʻamaʻa ʻana o nā mea hoʻohuihui i ka hopena mechanical o nā mea ma lalo o kekahi mau kūlana, ʻokoʻa loa ia mai nā hopena hoʻokolohua ma lalo o nā kūlana quasi-static. ʻO ka hana noiʻi nui o kēia manawa ʻo ia ka hopena o ka wela maʻemaʻe (me ka hoʻokomo ʻana i ka wai) ma ka haʻahaʻa haʻahaʻa haʻahaʻa o ka hopena o ka fiber reinforced resin matrix composites. Ua aʻo ʻo Pan Wenge et al [10] i nā waiwai hoʻoemi o nā laminate fiberglass/epoxy composite i ulana ʻia ʻelua ma hope o ka hopena haʻahaʻa ma ka lumi wela a ma lalo o nā kūlana wela a me ka wai (65 °C wai immersion). 4. Loaʻa ka laminate ma lalo o ka wela a me ka humid ma hope o ka haʻahaʻa haʻahaʻa haʻahaʻa. Hoʻemi nui ʻia ka hana hoʻoemi. ʻO Karasek et al. [1] ua aʻo i ka hopena o ka haʻahaʻa a me ka wela ma ka hopena o nā graphite/epoxy composites, a loaʻa iā lākou ma nā wahi wela haʻahaʻa a me ka lumi wela. He liʻiliʻi ka hopena o ka haʻahaʻa i ka ikehu mua a me ka lawe ʻana i ka ikehu o ka pōʻino. Ua hana ʻo Yucheng zhong et al [12,13] i kahi hoʻokolohua haʻahaʻa haʻahaʻa haʻahaʻa ma nā laminates composite ma hope o ka mālama ʻana i ka wela. Ua manaʻo ʻia ʻo ka wela a me ka humid kaia e hoʻemi nui i ka pōʻino o ka laminate. E hoʻomaikaʻi i ka hopena o nā laminates. Krystyna et al. [14] aʻo i ka hopena haʻahaʻa haʻahaʻa o ka aramid-glass fiber/epoxy composite ma hope o ka mālama ʻana i ka wela pulu (70 °C wai immersion), a loaʻa kahi wahi pōʻino liʻiliʻi ma hope o ka mālama ʻana i ka wela. Hoʻopilikia kēia i ka pōʻino delamination i loko o ka hāpana, kahi e hoʻonui ai i ka ikehu i ka wā o ka hopena a pale i ka hoʻokumu ʻana o ka delamination. Hiki ke ʻike ʻia ma luna aʻe ka hopena o ka hopena o ka wela wela i ka hopena o ka pōʻino o nā mea hoʻohuihui he hopena hoʻoikaika a me ka hopena nāwaliwali. No laila, pono e noiʻi hou a hōʻoia. Ma ke ʻano o ka hopena, ua noi a hoʻokumu ʻo Mei Zhiyuan et al [15] i ʻelua-pae (ka ʻū ʻana a me ka hoʻomau ʻana i ke komo ʻana) hoʻohālikelike hoʻohālikelike hoʻohālikelike o nā laminates composite i hoʻoikaika ʻia i ka fiber ma lalo o ka hopena kiʻekiʻe. ʻO Guiping Zhao et al. [16] alakaʻi i ʻekolu ʻano o nā wikiwiki like ʻole (emi i ka, like a ʻoi aku ka nui o ka wikiwiki palena ballistic) ma ka hopena o ka hopena a me ka pōʻino o ka specimen ma hope o nā ʻano laminates ʻekolu, akā ʻaʻole i pili i ka hopena o ka ʻāina wela ma luna o ka pōʻino hopena. . Ma muli o ka palapala i luna, ʻaʻole i ʻimi hou ʻia ka noiʻi e pili ana i ka hopena o ka wai a me ka wela i ka fiber reinforced composite laminates. Ma kēia pepa, ua aʻo ʻia nā hiʻohiʻona pōʻino o ka pulu kalapona saturated carbon fiber/epoxy composite laminates ma lalo o 70 °C wai ʻauʻau wai. Ua kālailai ʻia nā hopena o ka ʻāina wela a me ka haʻahaʻa ma ka hopena o ka hopena o nā ʻano composites ma ka hoʻohālikelike ʻana me nā laʻana wela o ka lumi maloʻo. I ka hoʻokolohua, ua hoʻopili ʻia nā laminates CFRP ma nā laminates CFRP ma 45 m / s, 68 m / s a me 86 m / s. Ua ana ʻia ka wikiwiki ma mua a ma hope o ka hopena. Ua nānā ʻia ka mana o ka wela a me ka haʻahaʻa i ka hana ʻana o ka ikehu o nā laminates. Ua hoʻohana ʻia ka ultrasonic c-scan e ʻike i ka pōʻino o loko o ka laminate, a ua loiloi ʻia ka hopena o ka wikiwiki o ka hopena ma ka wahi i haʻi ʻia. Ua hoʻohana ʻia ka ʻōnaehana electron scanning a me ka ʻōnaehana microscopic ultra-depth-hohonu ʻekolu-dimensional e nānā i nā ʻano mesoscopic o ka pōʻino hāpana, a ua kālailai ʻia ka pōʻino o ka hāpana e ke kaiapuni wela humid. Ka hopena o nā hiʻohiʻona.
2 Nā mea hoʻokolohua a me nā ʻano hana
2. 1 Mea a me ka hoomakaukau ana
Carbon fiber epoxy resin (T300/EMl 12) composite material, pre-immersion i hāʻawi ʻia e Jiangsu Hengshen Co., Ltd., one-layer pre-immersion mānoanoa o 0. 137 mm me ka hapa nui o ka fiber o 66%. Hoʻomoeʻia ka papa laminate ma ka papahele o ka papa. , nui 115mm x 115mln. Hoʻohana ʻia ke kaʻina hana o ka pahu paʻi wela. Hōʻike ʻia ke kiʻina hana hoʻōla i hoʻomākaukau ʻia e ke kaʻina hana ma ke Kiʻi 1. E hoʻokiʻekiʻe mua i ka hale mai ka lumi wela a i 80 oC ma ka wikiwiki hoʻomehana o 1 a 3 oC/min, a laila e mahana no 30 min, wela i 130 oC ma kahi wela wela o ka l13 oC/min, mālama i ka mahana ma 120 min, hoʻemi i 600C ma ka hooluolu mau ana, a laila e wehe i ke kaomi a me ka hookuu, a hookuu.
2. 2 Wela wela wela
Ma hope o ka hoʻomākaukau ʻana o ka specimen, ua hoʻomaʻamaʻa ʻia ka hāpana e like me ka ʻōlelo kikoʻī HB 7401-96.171 "Resin-based composite layer wet warm environment moisture absorption experimental method". ʻO ka mua, hoʻokomo ʻia ka mea hoʻohālike i loko o kahi keʻena maloʻo thermostatic ma 70 degere C e maloʻo ai. Ke kaupaona mau nei me ka hoʻohana ʻana i nā kaulike a hiki i ka paʻa ʻana o ka maikaʻi o ka hōʻailona ma mua o 0. 02%, ʻo ka waiwai i hoʻopaʻa ʻia i kēia manawa ʻo Engineering Dry Mass G. Ma hope o ka maloʻo ʻana, waiho ʻia ka specimen i 70 degere C o ka wai no ka mālama wela wela. E like me ka kikoʻī HB 7401. ʻO ke ʻano i hōʻike ʻia ma 96 "ana i ka maikaʻi o ka specimen i kēlā me kēia lā, i hoʻopaʻa ʻia e like me Gi, a hoʻopaʻa i ka hoʻololi ʻana o ka moisture absorption Mi.
Hōʻike ʻia ke ʻano: ʻO Mi ka hoʻoheheʻe ʻana o ka mea hoʻohālike, ʻo Gi ka maikaʻi ma hope o ka hoʻomoʻa ʻana o ka hāpana i ka wai, g, hele ka maikaʻi maloʻo o ka ʻenekinia specimen.
2. 3 Hoao Hoao
Ua hoʻokō ʻia ka hoʻokolohua hopena kiʻekiʻe ma ka CFRP laminate ma luna o kahi pūkuniahi ea kiʻekiʻe me ke anawaena o 15 mm. ʻO ka mea hana hoʻāʻo hopena hopena kiʻekiʻe (e nānā i ke Kiʻi 2) e loaʻa i ka pū ea holo wikiwiki, ka mea ana i ka laser ma mua a ma hope o ka hopena, ke kino pōkā, ka mea hoʻopili kikoʻī (ke kihi ʻākau o luna o ke Kiʻi 2), a me ka mea hoʻōla palekana kino pōkā. ʻO ke kino o ka pōkā he pōkā poʻo cone-headed (Figure 2), a ʻo ka nui o ka pōkā he 24. 32 g me ke anawaena o 14. 32 mm; ʻO ka wikiwiki o ka hopena he 45 m/s (ka ikehu hopena 46 J), 68 m/s (ka ikehu hopena 70 J), 86 m/s (ka ikehu hopena 90 J) hopena.
2. 4 ʻIke pōʻino o nā specimens
Ma hope o ka pili ʻana i ka hopena, ua hoʻohana ʻia ka ʻāpana kalapona kala epoxy composite composite laminate layer edgout plate e ʻike i ka pōʻino o loko o ka pā laminate CFRP, a ua ana ʻia ka wahi projection o ka hopena pōʻino e ka polokalamu loiloi kiʻi UTwim, a ʻike ʻia nā hiʻohiʻona kikoʻī o ka luku cross-sectional e ka nānā ʻana i ka microscope electron microscope a me ka ʻōnaehana ultra-3D.
3 Nā hopena a me nā kūkākūkā
3. 1 Nā hiʻohiʻona hiʻohiʻona hoʻoheheʻe wai
ʻO ka huina o 37. 7 d, ʻo ka awelika o ka hoʻoheheʻe ʻana i ka wai maʻemaʻe he 1. 780%, me ka nui o ka diffusion o 6. 183x10. 7lllnl2/s. Hōʻike ʻia ke kiʻi hoʻoheheʻe wai o ka CFRP laminate specimen ma ka Figure 3. E like me ka mea i ʻike ʻia mai ka Figure 3, ʻo ka laina o ka ulu mua ʻana o ka hoʻoheheʻe ʻana o ka wai o ka specimen he laina laina, ma hope o ka pae laina, hoʻomaka ka ulu ʻana o ka hoʻoheheʻe ʻana i ka wai e emi iho, a hiki i kahi kūlana paʻa23 d ka pae ma hope o ka hoʻopau ʻana o ka moisture. manawa. No laila, ʻo ka hoʻomaʻamaʻa ʻana o ka mea hoʻohālike e like me ke ʻano o ka hoʻoheheʻe ʻana o ka wai ʻelua: ʻo ka pae mua o ka hoʻoheheʻe ʻana ma muli o ka hana hui o ka mahana a me ka haʻahaʻa, ʻo ka wai ma o ka mea ponoʻī he pores, nā lua, nā māwae a me nā hemahema ʻē aʻe i hoʻolaha ʻia i loko o ka mea; Ua lohi ka hoʻoheheʻe wai a hiki i ka saturation ma kēia pae.
3. ʻO nā hiʻohiʻona luku o ka papa laminate 2-layer
Impact māmā holo o 86 m / s ka wā o ka specimen mua, ke kua o ka apparent luku profile palapala 'āina, ma ka maloʻo lumi wela hāpana, pulu wela saturation specimen mua luku shape ua oi like, ka elua specimens i ka hopena, ma muli o ke kahua māwae, kona luku ma ka papa mua o ka fiber i kekahi pahee. ʻO kēia ke kumu e hana ai ka mua i ke ʻano elliptic a i ʻole rectangular, a ma waho aʻe o ka hiki ke ʻike i ka māwae i loko o ka substrate, ʻike ʻia ka haki ʻana o nā fiber. Ma ke keʻena maloʻo wela hāpana, pulu wela saturation hāpana ma ke kua o ka luku ana o ke kinona hiki ke ike i ke kua ma ke ala hopena i kekahi bulge, a hoike mai i kea-like māwae. ʻIke ʻia ʻo ka haʻihaʻi ʻana o ka fiber, ka haʻihaʻi kumu a me ka haʻihaʻi interlayer (layering) ʻekolu ʻano o ka luku ʻana, ua hāpai ʻia ka ʻāpana hope o ka fiber akā ʻaʻole i haki, ʻo ka waiho wale ʻana a me ka māwae fiber/base. He ʻokoʻa hoʻi ka haʻihaʻi ʻana o ka fiber, e like me ka mea i ʻike ʻia mai ka hoʻohālikelike ʻana i ka pōʻino mua a me hope. ʻO ka mua ke kumu o ka haʻihaʻi ʻana o ka fiber a me ka substrate ma muli o ke kaomi ʻana a me ka ʻā. ʻO ke kua ma muli o ke kīkoʻo ʻana i haki ai ka fiber a kau i ka substrate. He 45 m/s, 68 m/s, 86 m/s ke kiʻi 4 i ka wā i hōʻino ʻia ai ke kino C scan. ʻO ka ʻāpana i hōʻike ʻia e ka laina poʻe l hina hina ma ke kikowaena o ke kiʻi, ʻo ia ka wahi i manaʻo ʻia o ka pōʻino. ʻO ka laina ʻeleʻele ma luna a ma lalo o kēlā me kēia pakuhi liʻiliʻi e hōʻike ana i ka wahi no ka ʻili hope o ka mea hoʻohālike. ʻO ka ʻāpana i kaha ʻia ma ka laina keʻokeʻo ma ke kiʻi (b) (d) (f) ʻo ia ka pōʻino o loko o ka specimen ma ka palena. Hōʻike ka pakuhi i ka piʻi ʻana o ka ikehu hopena i ka piʻi ʻana o ka wikiwiki o ka hopena. Hiki i ka pā laminated ke hoʻonui i ka ikehu i ka wā o ka hopena (e nānā i ke Kiʻi 6 no nā waiwai kikoʻī), e hoʻonui ana i kahi o ka laminate pōʻino projection: ma ka hoʻohālikelike ʻana i ka laʻana wela o ka lumi maloʻo me ke kiʻi o ka mea hoʻoheheʻe wela wela, hiki ke ʻike ʻia aia ka pōʻino o loko (laina keʻokeʻo) o ka mea hōʻike i hana ʻia ma ka palena o ke kaʻina hana wai a me ka wela o ke kaʻina. ʻO ka plasticization o ka substrate i loko o ka pā laminate a me ka nāwaliwali o ke kikowaena fiber-base ke kumu o ka palena i kahi hopena i ka pā laminate i ka wā o ka hopena hopena. Wahi a ke kiʻi, ʻaʻole ʻokoʻa loa ka ʻāpana peeling hope (laina ʻeleʻele) o ka specimen i kahi maloʻo maloʻo me ka mokuʻāina saturation wela.
3. ʻO nā hiʻohiʻona luku kikoʻī o ka 3-layer panel
ʻO ka palapala ʻāina o ka ʻaoʻao o ka papa hui CFRP, i lawe ʻia e ka ultra-depth 3D microsystem a me ke aniani electron scanning, me ka wikiwiki o ka hopena o 45 m / s, maloʻo a pulu a wela, e hōʻike ana i ka pōʻino o ka specimen ma nā mokuʻāina ʻelua he ʻekolu ʻano o ka luku: fiber fracture, base crack a interlayer fracture. Akā ʻokoʻa ke kumu o nā specimen ʻelua. ʻO ka haʻihaʻi ʻana o ka substrate i kahi maloʻo maloʻo ua haki ʻia ma ka pilina ma waena o ka fiber a me ka substrate. Eia nō naʻe, ʻo ka haki ʻana o ka substrate ma hope o ka mālama ʻana i ka wela wela e hele pū me nā ʻāpana o ka substrate e hāʻule ana i waho. Wold-esenbet a me nā mea ʻē aʻe i loko o ka wai a me ka wela o ka hopena o ka hana ʻana o ka hale a me ka fiber substrate interface degradation i hui pū ʻia, i loko o ka wai wela, CFRP layer plate i ka resin base ʻike absorption o kekahi nui o ka wai, e kahe ana ka wai e hoʻoheheʻe i ka resin substrate. ʻAʻole hiki ke hoʻopili ʻia ka carbon fiber, a laila pono e hoʻonui ʻia ma waena o nā mea ʻelua, hoʻonāwaliwali kēia ʻokoʻa i ka pilina ma waena o ka substrate a me ka fiber, e hōʻemi i ka ikaika o ka substrate. Ke hoʻokau ʻia i ka haʻahaʻa hopena, hoʻokuʻu maʻalahi nā ʻāpana substrate, e hopena i kahi ʻokoʻa mai ke keʻena maloʻo o ka lumi maloʻo. Mai ka kikoʻī kikoʻī o ke aniani uila scanned, hiki ke ʻike ʻia ʻo ka mahā o ka pulu a me ka wela post-base kino ʻo ia ka maʻa o ka haʻihaʻi paʻi, ʻoiai ʻo ka haʻihaʻi ʻana ma mua o ka wela wela ka mea maʻamau, a ʻoi aku ka maopopo o ka māwae ʻāʻī ma waena o nā papa. Mai ka microscope optical i ke kiʻi, hiki ke ʻike ʻia he ʻokoʻa nā ʻano luku i nā hihia ʻelua, a ʻo ke kūlana maloʻo ka luku ʻana i kēlā me kēia. No ka ʻoki ʻana i ka luku nui, ma hope o ka wela wela no ke ʻano o ka luku i hui pū ʻia me ka luku nui ʻana, ua hoʻonui ʻia ka hapa o ka luku ʻia. Hiki ke ʻike ʻia mai ke kihi o ka mīkini luku a me nā hiʻohiʻona absorption ikehu. Ua hoʻopuka mua ʻo Mei Zhiyuan i ʻelua mau ʻanuʻu o ka hoʻouka kaua projectile: ke kahua ʻoki a me ke kahua hoʻouka kaua mau. ʻO ka ʻāpana A i loko o ka laʻana wela wela ʻo ka shear intrusion stage luku, ʻoi loa no ka mea i ke kaʻina hana, ua hoʻopaʻa ʻia ka papa papa a hoʻopaʻa ʻia i ka hoʻokumu ʻia ʻana o ka deformation luku, ʻo ka ʻāpana ʻo ka luku mau ʻana i ke kahua. ʻO kēia kaʻina ma muli o ka emi ʻana o ka wikiwiki o ka intrusion kino o ka pōkā ma lalo o ka hana o ka ʻāpana koʻikoʻi o ka papa fibrous, a ua hoʻololi nui ʻia ka ikehu i loko o ka fiber stretch strain energy a me ka interlayer fracture ikehu (l 51), no laila ʻaʻole i ka laina pololei ka fiber break el. I ka hāpana maloʻo, ʻaʻole ʻike ʻia kēia ʻano, a ʻoi aku ka koʻikoʻi o ka pōʻino o ka pā, ʻoi aku ka maʻa o ka papa papa. 3. 4 Absorption ikehu a me damagehole projection wahi kālailai Figure 5 hōʻike i ka pilina ma waena o maloʻo lumi wela a pulu wela saturation o ka holo wikiwiki a me ka ikehu lilo o ke kino, ma ka hanana wikiwiki o ma kahi o 45 m / s, ka maloo lumi wela o ka poka a pau rebound, no laila,ʻaʻole i hōʻike 'ia ma ke kiʻi. E like me ka mea i ʻike ʻia mai ka Figure 7, i ka wā e hoʻāʻo ʻia ai ka hoʻāʻo ʻana ma lalo o ka saturation wela wela, ʻoi aku ka nui o ka nalowale o ka ikehu o ka pōkā, a piʻi ka hiki ke hoʻomoʻa i ka hāpana ma hope o ka mālama ʻana i ka wela.
ʻO ka Figure 6 he kiʻi paʻi kiʻi o ka ʻāpana kuhi o ka wikiwiki o ke kino pōkā a me ka lua pohō o ka papa CFRP (ʻo ka laina hina kahi ʻāpana o ke Kiʻi 4), ʻike ʻia ke kiʻi piha (4), (5), (6): (1) me ka piʻi ʻana o ka wikiwiki o ka hopena, piʻi ka CFRP layer layer pōʻino lua. hoʻonaʻauao; (3) inā he 45 m/s ka wikiwiki o ka hopena, ʻoi aku ka nui o ka ʻāpana o ka pōʻino o ka pā laminated ma hope o ka hoʻomaʻamaʻa ʻana i ka wela ma mua o ka ʻāpana projection o ka lua pōʻino o ka pā i loko o ka moku maloʻo. Wet thermal saturation sample poino l-hole projection wahi i hoonuiia e 85. 1% a ma ka haalulu wikiwiki o ma kahi o 68 m / s, ka laminated pā i loko o ka pulu a me ka thermal saturation moku'āina hoʻonui i 18. 10%, ka absorption waiwai (Figure 5) ma 15. 65%; Ma ka hopena o ka wikiwiki ma kahi o 88 m / s, ua hoʻemi ʻia ka pā laminated i loko o ka moku maloʻo a me ka thermal saturation e 9. 25%, ua hoʻonui ʻia ka waiwai absorption e 12. 45%.
Ma muli o nā hualoaʻa noiʻi o Yucheng Zhong a me nā huahana ʻē aʻe, ʻo ka hoʻomaʻamaʻa ʻana o nā mea i hoʻohui ʻia i ka carbon fiber-reinforced composite e hoʻomaikaʻi i ka palena elastic a me ka hopena o ka hopena o ka pā laminate, a hoʻohui i ka wahi i manaʻo ʻia o ka lua pōʻino o ka specimen wela o ka lumi maloʻo a me ka mea hoʻonaninani wela wela ma kēia pepa (Figure 4 i ka laina o ka pahu hana a me ka laina o ka papahana. hiki ke hoʻohālikelike i ka lua o ka papa CFRP, a hiki ke hoʻohālikelike ʻia ka pōʻino papa o ka papa hui CFRP i ka wā like a haʻahaʻa ka wikiwiki o ka hopena. ʻO ka ʻāpana pōʻino o ka mea hoʻoheheʻe wai wela wela he ʻano nui. ʻO kēia ma muli o ka hoʻomaʻamaʻa wela wela e hana ai ka CFRP layer substrate plasticization, nāwaliwali i ka fiber a me ka substrate interface a me ka hana interlayer, i ka hopena, ke kūlana saturation pulu wela o ka specimen layered pōʻino hoʻonui, hoʻonui ka nui o ka pōʻino. Ma muli o Wu Yixuan a me nā hoʻokolohua ʻē aʻe, ʻike ʻia ka ikaika o ka hopena i ke ala paving vertical e ka resin substrate, a laila ʻo ka plasticization o ka substrate e hoʻonui i ka ikehu a me ka wela o ka saturation specimen i ka wā o ka hopena, hoʻomaikaʻi i ka pale ʻana i ka hopena, a hoʻonui i ka wahi projection o ka lua pōʻino; ʻAʻole i hoʻolōʻihi ʻia ka pōʻino laminate CFRP, ua pau ka hopena, no laila ke piʻi aʻe ka wikiwiki o ka hopena, ʻaʻole koʻikoʻi ka mālama ʻana i ka wela wela ma ka CFRP laminate pōʻino projection area, akā ma muli o ka plasticization o ka resin substrate, ua hoʻonui ʻia ka mana absorption.
4 Manao
(1) Me ka piʻi ʻana o ka wikiwiki o ka hopena, piʻi ka laminate i manaʻo ʻia o ka lua pōʻino o ka carbon fiber reinforced epoxy resin composite (CFRP), a ʻoi aku ka kiʻekiʻe o ka ulu ʻana o ka pōʻino 孑L lua i loko o ka hāpana ma kahi mahana wela o ka lumi maloʻo. Nui: (2) Ke hoʻonui ʻia ka wikiwiki o ka hopena i 45 m / s, ua hoʻonui ʻia ka ʻāpana projection pōʻino o ka CFRP laminate i ka mokuʻāina saturation wela wela e 85. 11%, i ka 68 m / s ka wikiwiki o ka hopena, ua hoʻonui ʻia ka wahi projection pōʻino o ka CFRP laminate i ka mokuʻāina saturation wela wela i ka 18% maloʻo maloʻo i hoʻohālikelike ʻia me ka 18% maloʻo. 10%, ʻo ka wikiwiki o ka hopena he 86m / s. Hoʻemi ʻia ka wahi i hōʻino ʻia e ka cFRP laminate i hoʻomoʻa ʻia e 9.9% ke hoʻohālikelike ʻia me ka lumi maloʻo cFRP laminate. 25%; (3) Ma hope o ka hoʻopili ʻia ʻana o ka cFRP laminate e ka ʻāina wela a me ka haʻahaʻa, ua hoʻemi ʻia ka hana interlayer o ka laminate, ka hopena o ka hoʻonui ʻana i ka wahi delamination.
Ka manawa hoʻouna: Jun-24-2019